Characterization of superconducting BSCCO/CaSiO3 and BSCCO/CaZrO3 Ag PIT wires
Australian Institute for Innovative Materials - Papers
  • Natacha A Nogueira, Universidade Estadual Paulista
  • Anne H Yonamine, Universidade Estadual Paulista
  • Dayse I Dos Santos, Universidade Estadual Paulista
  • Jung Ho Kim, University of Wollongong
  • S X Dou, University of Wollongong
RIS ID
92691
Publication Date
1-1-2014
Publication Details

Nogueira, N. A., Yonamine, A. H., dos Santos, D. I., Kim, J. H. & Dou, S. X. (2014). Characterization of superconducting BSCCO/CaSiO3 and BSCCO/CaZrO3 Ag PIT wires. Advanced Materials Research, 975 106-110.

Abstract
The addition of two compounds, calcium silicate and calcium zirconate was tested, in the preparation of Bi: 2212 silver sheathed wires by powder-in-tube method, which were successfully tested previously in processing chips. The wires were treated in an atmosphere of O2/Ar using partial melting method. The characterizations were structural and on their electrical and magnetic properties. As the results, transition temperatures were higher than the expected for this stage, ranged from 105K (BSCCO880) to 116K (+Si883). The critical current densities encountered in transport and magnetization measurements were improved in comparison with the wires without addition.