Highly porous hematite nanorods prepared via direct spray precipitation method
Australian Institute for Innovative Materials - Papers
  • Dean Cardillo, University of Wollongong
  • Moeava Tehei, University of Wollongong
  • Michael L. F Lerch, University of Wollongong
  • Stephanie Corde, University of Wollongong
  • Anatoly B Rosenfeld, University of Wollongong
  • Konstantin K Konstantinov, University of Wollongong
RIS ID
86693
Publication Date
1-1-2014
Publication Details

Cardillo, D., Tehei, M., Lerch, M., Corde, S., Rosenfeld, A. & Konstantinov, K. (2014). Highly porous hematite nanorods prepared via direct spray precipitation method. Materials Letters, 117 279-282.

Abstract

Hematite nanoparticles can be formed through a variety of synthesis routes, each of which can substantially affect the properties of the resulting product. In this article we report the use of a facile synthesis route, direct spray precipitation, and compare the performance of these α-Fe2O 3 products with those obtained through standard precipitation method. Through this new method, we obtain a nanocrystalline α-FeO(OH) precursor material, while an amorphous material is obtained from precipitation route. The highly efficient, low temperature (300 C) calcination of this nanocrystalline precursor results in the formation of hematite nanorods with a diameter between 20 and 30 nm. These nanorods exhibit an extremely high surface area (up to 166 m2 g-1) attributed to their morphology and apparent nanoporosity. This very high surface area coupled with higher attenuation in the ultraviolet-visible with a low temperature synthesis give this material potential for further investigation as photocatalyst or energy storage material. 2013 Elsevier B.V.