A Comprehensive Structural Analysis Process for Failure Assessment in Aircraft Lap-Joint Mimics using Intramodal Fusion of Eddy Current Data
Research in Nondestructive Evaluation
  • Soumya De
  • Kapil Gupta
  • R. Joe Stanley, Missouri University of Science and Technology
  • R. Zoughi, Missouri University of Science and Technology
  • Kenneth Doering
  • David C. Van Aken, Missouri University of Science and Technology
  • Gary Steffes
  • Matthew O'Keefe, Missouri University of Science and Technology
  • Donald D. Palmer
Abstract

In the aerospace industry, nondestructive evaluation (NDE) techniques are commonly used for structural health monitoring, including finding manufacturing and service-induced discontinuities and defects such as corrosion and cracks. A comprehensive structural analysis process is presented for quantizing and evaluating characteristics of aircraft lap-joint mimics. The process investigated here consists of NDE data acquisition, defect detection and characterization involving material loss estimation, three-dimensional structural model generation, finite-element modeling to simulate fatigue damage and comparison with actual tensile fatigue-induced structural analysis data (mechanical loading). The structural analysis process is examined using five test panels consisting of stacked and riveted aluminum plates, configured as lap-joints, four of them with different corroded patches at different layers of the lap-joints and one painted pristine panel used as a reference. The test panels were subjected to three rounds of incremental and cyclical tensile fatiguing with the final round resulting in complete fatigue failure. Eddy current data was obtained from the test panels prior to each round of mechanical loading. Comparing the simulated fatigue loading and the mechanical loading results for identifying susceptible-to-failure areas on the test panels, this comprehensive structural analysis process found the correct location of failure areas at rates as high as 88.9%.

Department(s)
Electrical and Computer Engineering
Second Department
Materials Science and Engineering
Keywords and Phrases
  • Aging aircraft,
  • Aluminum plates,
  • Defect detection and characterization,
  • Failure assessment,
  • Fatigue failures,
  • Fatigue loadings,
  • Finite element modeling,
  • Intramodal fusion,
  • Material loss,
  • Mechanical loading,
  • Non destructive evaluation,
  • Non-destructive evaluation techniques,
  • Structural models,
  • Test panels,
  • Aerospace industry,
  • Aircraft,
  • Cracks,
  • Data fusion,
  • Eddy current testing,
  • Fatigue of materials,
  • Model structures,
  • Structural analysis,
  • Structural health monitoring,
  • Three dimensional,
  • Loading,
  • aging aircraft,
  • aircraft lap-joints,
  • fatigue,
  • nondestructive evaluation,
  • structural health monitoring (SHM)
Document Type
Article - Journal
Document Version
Citation
File Type
text
Language(s)
English
Rights
© 2012 Taylor & Francis, All rights reserved.
Publication Date
7-1-2012
Publication Date
01 Jul 2012
Citation Information
Soumya De, Kapil Gupta, R. Joe Stanley, R. Zoughi, et al.. "A Comprehensive Structural Analysis Process for Failure Assessment in Aircraft Lap-Joint Mimics using Intramodal Fusion of Eddy Current Data" Research in Nondestructive Evaluation Vol. 23 Iss. 3 (2012) p. 146 - 170 ISSN: 0934-9847
Available at: http://works.bepress.com/reza-zoughi/9/