A Young's modulus study of n- and p-type porous silicon
physica status solidi (a)
  • Michael K Oisten, Michigan Technological University
  • Paul L. Bergstrom, Michigan Technological University
Document Type
Article
Publication Date
3-30-2009
Abstract

With the number of MEMS based applications utilizing porous silicon increasing, it has become more important to know the mechanical properties of the material. Using nanoindentation, the Young's modulus of various n-type and p-type mesoporous silicon samples has been measured. The porous silicon samples were produced by electrochemical anodization in an ethanoic hydrofluoric acid solution. Anodization conditions were varied to study the impact on Young's modulus due to porosity and pore morphology. The current densities of the p-type samples were varied between 20 mA/cm2 and 60 mA/cm2 and the n-type samples current densities were varied between 3 mA/cm2 and 60 mA/cm2. The investigation demonstrated a strong morphological change for n-type samples which caused a much broader range of Young's modulus values measured. It was also observed that the p-type samples pore morphologies did not significantly change over the range of current densities used, therefore the changes in the Young's modulus can be attributed to a change in porosity.

Publisher's Statement

© 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Publisher's version of record: http://dx.doi.org/10.1002/pssa.200881096

Citation Information
Michael K Oisten and Paul L. Bergstrom. "A Young's modulus study of n- and p-type porous silicon" physica status solidi (a) Vol. 206 Iss. 6 (2009) p. 1278 - 1281
Available at: http://works.bepress.com/paul-bergstrom/13/