Stress-Optical behavior of Poly (m-xylylenediamine adipamide)(Nylon MXD6): Influence of molecular weight
  • Sylvian Seif
  • Mukerrem Cakmak
Document Type
Publication Date
The effect of molecular weight and rubbery state uniaxial stretching conditions on the mechano-optical behavior of Poly(m-xylylenediamine adipamide) (Nylon MXD6) films was investigated using a real time spectral birefringence stretching machine. The stress optical behavior exhibits a multi stage behavior that depends on process conditions as well as molecular weight. At low stretching temperatures and high rates the stress optical behavior was found to start with an initial glassy photo elastic behavior. Decreasing stretching rate or increasing processing temperature was found to eliminate this glassy photoelastic regime leading to the observation of a linear initial stress optical behavior past a temperature of 95 °C (Tll). The stress optical constant (SOC) was about the same for both M.W. materials stretched at temperatures past Tll, at 2.7 GPa−1 for HPA6 and 2.61 GPa−1 for LPA6. Following this initial regime, the behavior is controlled by the competition between orientation and relaxation during deformation. If the chain orientation relaxation is not suppressed by increasing the stretching rate and/or the molecular weight or by decreasing temperature, the material strain crystallizes.
Citation Information
Sylvian Seif and Mukerrem Cakmak. "Stress-Optical behavior of Poly (m-xylylenediamine adipamide)(Nylon MXD6): Influence of molecular weight" Polymer Vol. 51 Iss. 16 (2010) p. 3762 - 3773
Available at: