Thermo-Electromechanical Behavior of Piezoelectric Nanofibers
ACS Applied Materials and Interfaces (2016)
  • Mahmoud Baniasadi, Georgia Southern University
  • Zhe Xu, University of Texas at Dallas
  • Seokjin Hong, Texas A&M University
  • Mohammad Naraghi, Texas A&M University
  • Majid Minary-Jolandan, University of Texas at Dallas
High performance piezoelectric devices based on arrays of PVDF-TrFE nanofibers have been introduced in the literature for a variety of applications including energy harvesting and sensing. In this Research Article, we utilize uniaxial tensile test on arrays of nanofibers, microtensile, and nanoindentation and piezo-response force microscopy (PFM) on individual nanofibers, as wells as DSC, XRD, and FTIR spectroscopy to investigate the effect of annealing on microstructure, mechanical, and piezoelectric properties of arrays and individual electrospun nanofibers. For PVDF-TrFE nanofibers annealing in a temperature between the Curie and melting temperature (in paraelectric phase) results in ∼70% increase in crystallinity of the nanofibers. The findings of our multiscale experiments reveal that this improvement in crystallinity results in ∼3-fold increase in elastic modulus, and ∼55% improvement in piezoelectric constant. Meanwhile, the ductility and tensile toughness of the nanofibers drop by ∼1 order of magnitude. In addition, nanoscale cracks were observed on the surface of the annealed nanofibers; however, they did not result in significant change in the strength of the nanofibers. The results of this work may have important implications for applications of PVDF-TrFE in energy harvesting, biomedical, and sensor areas.
  • Annealing,
  • Crystallization,
  • Electrospinning,
  • Electrospun nanofiber,
  • Mechanical properties,
  • Multifunctional polymer,
  • Piezoelectric properties,
Publication Date
January 11, 2016
Citation Information
Mahmoud Baniasadi, Zhe Xu, Seokjin Hong, Mohammad Naraghi, et al.. "Thermo-Electromechanical Behavior of Piezoelectric Nanofibers" ACS Applied Materials and Interfaces Vol. 8 Iss. 4 (2016) p. 2540 - 2551 ISSN: 1944-8252