Microscopic Observations of Voids in Anodic Oxide Films on Aluminum
Journal of The Electrochemical Society
  • R. Huang, Iowa State University
  • Kurt R. Hebert, Iowa State Univ,
  • L. Scott Chumbley, Iowa State University
Document Type
Publication Date
The relationship was explored between nanoscale voids in anodic aluminum oxide films and the surface condition of aluminum samples prior to anodizing. Transmission electron microscopy (TEM) detected voids on the order of 10 nm in anodic films. Atomic force microscopy (AFM) of these films, obtained after partial oxide dissolution, revealed surface cavities; comparison of TEM and AFM suggested that the cavities were the oxide voids. AFM images after variable extents of oxide dissolution showed that the voids were distributed evenly through the inner 60% of the film thickness, indicating that they were formed at the metal-oxide interface during film growth. Both AFM and TEM showed that the void concentration in the film was sensitive to the extent of dissolution of the aluminum samples in NaOH prior to anodizing. Positron annihilation spectroscopy had previously detected voids in samples without anodic films, located in the metal near the oxide-metal interface; the quantity of these interfacial voids was controlled by NaOH dissolution. The void concentration in the inner part of the anodic films was proportional to the quantity of these pre-existing interfacial voids. It was inferred that the oxide voids were formed by incorporation, during anodizing, of interfacial metal voids into the oxide film. The uniform concentration of oxide voids in the inner film suggested that interfacial metal voids formed continuously during anodizing and that metal voids were generated repeatedly at specific interfacial sites during film growth.

This article is from Journal of The Electrochemical Society 151 (2004): 379-386, doi: 10.1149/1.1753582.

Copyright Owner
The Electrochemical Society
File Format
Citation Information
R. Huang, Kurt R. Hebert and L. Scott Chumbley. "Microscopic Observations of Voids in Anodic Oxide Films on Aluminum" Journal of The Electrochemical Society Vol. 151 Iss. 7 (2004) p. 379 - 386
Available at: