Preparation and Instability of Nanocrystalline Cuprous Nitride
Inorganic Chemistry
  • Malinda D. Reichert, Iowa State University
  • Miles A. White, Iowa State University
  • Michelle J. Thompson, Iowa State University
  • Gordon J. Miller, Iowa State University
  • Javier Vela, Iowa State University
Document Type
Publication Version
Published Version
Publication Date
Low-dimensional cuprous nitride (Cu3N) was synthesized by nitridation (ammonolysis) of cuprous oxide (Cu2O) nanocrystals using either ammonia (NH3) or urea (H2NCONH2) as the nitrogen source. The resulting nanocrystalline Cu3N spontaneously decomposes to nanocrystalline CuO in the presence of both water and oxygen from air at room temperature. Ammonia was produced in 60% chemical yield during Cu3N decomposition, as measured using the colorimetric indophenol method. Because Cu3N decomposition requires H2O and produces substoichiometric amounts of NH3>, we conclude that this reaction proceeds through a complex stoichiometry that involves the concomitant release of both N2 and NH3. This is a thermodynamically unfavorable outcome, strongly indicating that H2O (and thus NH3 production) facilitate the kinetics of the reaction by lowering the energy barrier for Cu3N decomposition. The three different Cu2O, Cu3N, and CuO nanocrystalline phases were characterized by a combination of optical absorption, powder X-ray diffraction, transmission electron microscopy, and electronic density of states obtained from electronic structure calculations on the bulk solids. The relative ease of interconversion between these interesting and inexpensive materials bears possible implications for catalytic and optoelectronic applications.

Reprinted (adapted) with permission from Inorganic Chemistry 54 (2015): 6356, doi: 10.1021/acs.inorgchem.5b00679. Copyright 2015 American Chemical Society.

Copyright Owner
American Chemical Society
File Format
Citation Information
Malinda D. Reichert, Miles A. White, Michelle J. Thompson, Gordon J. Miller, et al.. "Preparation and Instability of Nanocrystalline Cuprous Nitride" Inorganic Chemistry Vol. 54 Iss. 13 (2015) p. 6356 - 6362
Available at: