Synthesis and Characterization of Sr-and Mg-doped LaGaO_3 Powders by Polyvinylpyrrolidone Microwave-induced Solution Polymerization
Journal of Functional Materials and Devices
  • Chang Ye, University of Akron, Main campus
  • Yuling Zhai
  • Jian-zhong Xiao
Document Type
Article
Publication Date
4-1-2007
Abstract
A new chemical route,named microwave-induced polyvinylpyrrolidone(PVP) solution polymerization,has been used to prepare La0.8Sr0.2Ga0.83Mg0.17O2.815(denoted as LS0.2GM0.17) powder.The effect of different contents of PVP as the polymeric carrier was studied and we obtained the optimum amount of PVP,which could ensure the homogenous distribution of the metal ions in its polymeric network structure and inhibit their segregation from the solution.The behavior of the powder after calcination at different temperatures was studied.The PVP solution process consumed less organics compared with traditional Pechini process.Consequently,PVP was a more effective carrier in the preparation of LSGM.High heating rate and more homogenous heating manner without thermal gradient in the microwave oven resulted in less secondary phases in the LS0.2GM0.17 powder after calcination at 1400℃ for 9 h and smaller pellet grain size(2-3μm) without segregation.
Citation Information
Chang Ye, Yuling Zhai and Jian-zhong Xiao. "Synthesis and Characterization of Sr-and Mg-doped LaGaO_3 Powders by Polyvinylpyrrolidone Microwave-induced Solution Polymerization" Journal of Functional Materials and Devices Vol. 13 Iss. 4 (2007) p. 323
Available at: http://works.bepress.com/chang_ye/31/