Interfacial Properties of Free-Standing Poly(3-hexyl thiophene) Films
The Journal of Chemical Physics
  • Yeneneh Y. Yimer
  • Ali Dhinojwala, The University Of Akron
  • Mesfin Tsige, The University Of Akron
Document Type
Article
Publication Date
10-1-2012
Abstract
Using full atomistic classical molecular dynamics simulations, the interfacial properties of free-standing poly(3-hexylthiophene) (P3HT) films have been investigated. The orientations of different parts of the P3HT chain and the surface tensions of the films were calculated in a temperature range of 540 K-600 K. At the liquid/vacuum interface, the P3HT chain shows ordering by exposing hexyl groups at the interface, while the chain backbone lays flat with the thiophene ring preferentially tilt toward the surface. At the interface, the terminal methyl groups of hexyl side chains are in excess compared to the methylene groups or thiophene rings. The surface tension of P3HT in its melt state shows similar temperature dependence to that of polymers that have long alkyl side chains. The surface tension values are comparable to those polymers that expose methyl or methylene groups on the surface. The surface tension values determined for the melt state are lower than the experimental reported values for crystalline P3HT films, as expected.
Citation Information
Yeneneh Y. Yimer, Ali Dhinojwala and Mesfin Tsige. "Interfacial Properties of Free-Standing Poly(3-hexyl thiophene) Films" The Journal of Chemical Physics Vol. 137 (2012)
Available at: http://works.bepress.com/ali_dhinojwala/84/